1. The generation of oxides during high temperature sliding wear does not automatically lead to the production of a compacted oxide layer'glaze '.
2. Limited interest has been shown in low friction properties of compacted oxide glaze layers formed at several hundred degrees Celsius in metallic sliding systems.
3. A further phenomenon that has undergone investigation in relation to high temperature wear prevention and lubrication, is that of a compacted oxide layer glaze formation.
4. Such high-temperature corrosion products, in the form of compacted oxide layer glazes, prevent or reduce wear during high-temperature sliding contact of metallic ( or metallic and ceramic ) surfaces.
5. Limited interest has been shown in low friction properties of compacted oxide glaze layers formed at several hundred degrees Celsius in metallic sliding systems, however, practical use is still many years away due to their physically unstable nature.
6. It's difficult to find compacted oxide in a sentence. 用compacted oxide造句挺难的
7. A change in conditions may also see a switch from the formation of a loose, abrasive oxide to the formation of wear protective compacted oxide glaze layers and vice versa, or even the reappearance of adhesive or severe wear.
8. As oxide generated is effectively the result of the tribochemical decay of one or both of the metallic ( or ceramic ) surfaces in contact, the study of compacted oxide layer glazes is sometimes referred to as part of the more general field of high temperature corrosion.
9. This is the generation of a compacted oxide layer which sinters together to form a crystalline'glaze'( not the amorphous layer seen in pottery ) generally at high temperatures, from metallic surfaces sliding against each other ( or a metallic surface against a ceramic surface ).
10. Any product where one material slides or rubs over another is affected by complex tribological interactions, whether lubricated like hip implants and other artificial prostheses, or unlubricated as in high temperature sliding wear in which conventional lubricants cannot be used but in which the formation of compacted oxide layer glazes have been observed to protect against wear.